Industrial aluminum, also known as: industrial aluminum extrusion guide and industrial aluminum alloy profile, is an alloy material with aluminum as the main component. Aluminum bars are hot-melt and extruded to obtain aluminum materials with different cross-section shapes, but the proportion of the added alloy is different, so are the mechanical properties and application fields of the industrial aluminum profile. The executive standard shall be in accordance with GB / t5237.1-2004. Generally speaking, industrial aluminum profiles refer to all aluminum profiles except for building doors and windows, curtain walls, indoor and outdoor decoration and building structures.
Brands of industrial aluminum:
1050 extrusion coil for food, chemical and brewing industry, various hoses, fireworks powder
1060 requires high corrosion resistance and formability, but not high strength. Chemical equipment is its typical use
1100 for processing parts and components that need good formability and high corrosion resistance but do not need high strength, such as chemical products, food industry devices and storage containers, sheet metal processing parts, deep drawing or spinning concave vessels, welding parts, heat exchanger, printed boards, nameplates, reflective devices
1145 packaging and heat insulation aluminum foil, heat exchanger
1199 electrolytic capacitor foil, optical reflective deposition film
1350 wire, conducting strand, busbar, transformer strip
2011 screws and machining products with good cutting performance
2014 shall be used in occasions requiring high strength and hardness (including high temperature). Aircraft heavy, forging, thick plate and extrusion materials, wheels and structural elements, first stage fuel tank and spacecraft parts of multistage rocket, truck frame and suspension system parts
2017 is the first 2XXX series alloy to obtain industrial application, with narrow application range, mainly including rivets, general mechanical parts, structure and transport tool structure parts, propeller and accessories
2024 aircraft structure, rivets, missile components, truck hub, propeller components and other structures
2036 auto body parts
2048 aerospace structure parts and weapon structure parts
2124 aerospace structure
2218 aircraft engine and diesel engine piston, aircraft engine cylinder head, jet engine impeller and compressor ring
2219 space rocket welding oxidant tank, supersonic aircraft skin and structural parts, operating temperature of - 270 ~ 300 ℃. Good weldability, high fracture toughness, high resistance to stress corrosion cracking in T8 state
2319 welding rod and filler metal of 2219 alloy
2618 die forgings and free forgings. Piston and Aeroengine Parts
2a01 structural rivets with working temperature less than or equal to 100 ℃
2A02 axial compressor blades for turbojet engines operating at 200-300 ° C
2A06 aircraft structure with working temperature of 150-250 ° C and rivets with working temperature of 125-250 ° C
2a10 has higher strength than 2a01 alloy, and is used to manufacture aircraft structural rivets with working temperature less than or equal to 100 ℃
2A11 aircraft's medium strength structural parts, propeller blades, transportation vehicles and building structural parts. Medium strength bolts and rivets for aircraft
2A12 aircraft skin, partition frame, wing rib, wing beam, rivet, etc., structural parts of buildings and transportation vehicles
2A14 free forging and die forging with complex shape
2A16 aerospace parts with working temperature of 250-300 ℃, welded containers and airtight cockpit working at room temperature and high temperature
2a17 aircraft parts with operating temperature of 225-250 ° C
2A50 medium strength parts with complex shape
2a60 aircraft engine compressor wheel, guide wheel, fan, impeller, etc
2A70 aircraft skin, aircraft engine piston, guide wheel, wheel plate, etc
2A80 aeroengine compressor blades, impellers, pistons, expansion rings and other parts with high operating temperature
2A90 aeroengine piston
3003 is used to process parts with good formability, high corrosion resistance and weldability, or requires both these properties and work with higher strength than 1xxx series alloy, such as kitchen utensils, food and chemical product processing and storage devices, tanks and tanks for transporting liquid products, and various pressure vessels and pipes processed with thin plates
3004 all aluminum can body requires parts with higher strength than 3003 alloy, chemical product production and storage device, sheet metal processing parts, building processing parts, building tools, various lighting parts
3105 room partition, baffle, movable room board, eaves gutter and downpipe, sheet metal forming parts, bottle cap, bottle plug, etc
3A21 aircraft oil tank, oil way conduit, rivet wire, etc.; industrial equipment such as building materials and food, etc
5005 is similar to 3003 alloy, with medium strength and good corrosion resistance. Used as conductor, cooker, dashboard, shell and building decoration. The anodized film is brighter than that on alloy 3003, and the color of anodized film is consistent with that of Alloy 6063
5050 sheet can be used as the inner lining of refrigerator and refrigerator, automobile gas pipe, oil pipe and agricultural irrigation pipe, and can also process thick plate, pipe, bar, special-shaped material and wire rod, etc
5052 alloy has good formability, corrosion resistance, candlelight, fatigue strength and medium static strength. It is used to manufacture aircraft oil tank, oil pipe, sheet metal parts of traffic vehicles and ships, instrument, street lamp bracket and rivets, hardware products, etc
5056 magnesium alloy and cable sheath rivets, zippers, nails, etc.; aluminum coated wire is widely used in the processing of agricultural insect catcher covers, as well as other occasions requiring high corrosion resistance
5083 is used for occasions requiring high corrosion resistance, good weldability and medium strength, such as welding parts of ship, automobile and aircraft plates; pressure vessels, cooling devices, TV towers, drilling equipment, transportation equipment, missile components, armor, etc. requiring strict fire protection
5086 is used for occasions requiring high corrosion resistance, good weldability and medium strength, such as warship, automobile, aircraft, low temperature equipment, TV Tower, drilling equipment, transportation equipment, missile parts and deck, etc
5154 welding structure, storage tank, pressure vessel, ship structure and marine facilities, transportation tank
5182 sheet is used to process parts such as can cover, auto body panel, control panel, reinforcement, bracket, etc
5252 is used to manufacture decorative parts with high strength, such as automobiles. Bright and transparent oxide film after anodizing
5254 containers for hydrogen peroxide and other chemical products
Aluminium magnesium alloy welding rod and wire with more than 3% magnesium content
5454 welded structure, pressure vessel, offshore facilities pipeline
5456 armor plate, high strength welded structure, storage tank, pressure vessel, ship material
5457 automotive and other equipment trims polished and anodized
5652 storage container for hydrogen peroxide and other chemical products
5657 automotive and other equipment trims that have been polished and anodized, but in any case must ensure that the material has fine grain structure
5A02 aircraft oil tank and conduit, welding wire, rivet, ship structure
5A03 medium strength welding structure, cold stamping parts, welding vessel, welding wire can be used to replace 5A02 alloy
5A05 welded structure, aircraft skin framework
5A06 welding structure, cold forging parts, welding and pulling vessel stress parts, aircraft skin and bone parts
5A12 welded structure, bullet proof deck
6005 extruded profiles and pipes are used for structural parts with strength higher than 6063 alloy, such as ladder, TV antenna, etc
6009 auto body panel
6010 sheet: car body
6061 requires various industrial structures with high strength, weldability and corrosion resistance, such as pipes, bars, shapes and plates for manufacturing trucks, tower buildings, ships, trams, furniture, mechanical parts, precision processing, etc
6063 industrial profiles, building profiles, irrigation pipes and extrusion materials for vehicles, stands, furniture, fences, etc
6066 forging and welding structure extrusion materials
6070 heavy load welding structure and extrusion materials and pipes for automobile industry
6101 high strength bar, electric conductor and heat sink for bus
6151 is used for die forging of crankshaft parts, machine parts and production of rolling rings, which requires good malleability, high strength and good corrosion resistance
6201 high strength conductive bar and wire
6205 thick plate, pedal and high impact extrusion
6262 high stress threaded parts with corrosion resistance better than alloy 2011 and 2017
6351 extrusion structure of vehicle, water, oil, etc
6463 building and various appliance profiles, as well as automobile decorative parts with bright surface after anodizing
6A02 aircraft engine parts, forgings and die forgings with complex shapes
7005 extrusion material is used for manufacturing welded structures with high strength and high fracture toughness, such as trusses, bars and containers of transportation vehicles; large heat exchangers, and parts that can not be solidified after welding; it can also be used for manufacturing sports equipment, such as tennis rackets and softball bats
7039 freezing container, low temperature apparatus and storage box, fire pressure apparatus, military apparatus, armor plate, missile device
7049 is used to forge parts with the same static strength as 7079-t6 alloy and high stress corrosion cracking resistance, such as aircraft and missile parts landing gear hydraulic cylinder and extrusion parts. The fatigue property of the parts is about the same as that of 7075-T6 alloy, but the toughness is slightly higher
7050 aircraft structural parts are made of medium and thick plates, extrusions, free forgings and die forgings. The requirements for manufacturing such parts are: high resistance to peeling corrosion, stress corrosion cracking, fracture toughness and fatigue resistance
7072 air conditioner aluminum foil and ultra thin strip; 2219, 3003, 3004, 5050, 5052, 5154, 6061, 7075, 7475, 7178 alloy plate and pipe coating
7075 is used to manufacture aircraft structure and other high stress structural parts and moulds with high strength and corrosion resistance.
7175 is a high strength structure for forging aircraft. T736 material has good comprehensive properties, i.e. high strength, peeling corrosion resistance, stress corrosion cracking resistance, fracture toughness and fatigue strength
7178 parts for aerospace manufacturing requiring high compressive yield strength
7475 fuselage with and without aluminum clad plate, wing frame, truss, etc. Other parts with high strength and high fracture toughness
7A04 aircraft skin, screws, and load-bearing components such as girder truss, spacer frame, wing rib, landing gear, etc
"Customer first, service first, innovation first" as the company's business philosophy, constantly strive to surpass ourselves; in business activities, the company ensures equality and mutual benefit, reliable quality, timely delivery, reasonable price and thoughtful service.
COMPANY:Fujian MingLv Aluminum Co., Ltd.
Contact:Mr. ZHENG
Tel:+86-0592-5718928
Phone:+86-13779947258
Email:120514135@qq.com
Add:No.44 hongcuoli, Dongren Road, Jimei District, Xiamen, China